LLDPE Geomembrane

Introduction

GM SL series of geomembranes is manufactured from Linear Low Density Polyethylene resins. The surfaces of both sides are smooth. The products are manufactured by the technology of coextrusion-blown triple layer.

Performance

Excellent prolongation performance in unidirection and multi directions, flexibility, good deformation adaptability, high puncture resistance, high aging resistance, high UV resistance, anti-acid & alkali, excellent low & high temperature resistance, innocuous, perfect water proof performance, seepage and humidity resistance and easy welding and constrution etc.

Application

The public works seepage projects of culvert, canal, reservoir, gardens and building etc.

Specifications

Width: 2000~7000mm
Thickness: 0.5~3.0mm

Voluntary Standards

GRI-GM17

Properties

Properties	Test Method	GM SL050	GM SL075	GM SL100	GM SL125
Thickness	D5199	0.50 mm	0.75 mm	1.00 mm	1.25 mm
Density	D1505	0.939 g/cc	0.939 g/cc	0.939 g/cc	0.939 g/cc
Tensile Properties 1. Break strength 2. Break elongation	D6693 Type IV	13 kN/m 700%	20 kN/m 800%	27 kN/m 800%	33 kN/m 800%
Tear Resistance	D1004	50 N	70 N	100 N	120 N
Puncture Resistance	D4833	120 N	190 N	250 N	310 N
Carbon Black Content -%	D1603	2.0%	2.0%	2.0%	2.0%
Carbon Black Dispersion	D5596	Note (1)	Note (1)	Note (1)	Note (1)
Oxidative Induction Time (OIT)	D3895	100 min.	100 min.	100 min.	100 min.

Properties	Test Method	GM SL150	GM SL200	GM SL250	GM SL300
Thickness	D5199	1.50 mm	2.00 mm	2.50 mm	3.00 mm
Density	D1505	0.939 g/cc	0.939 g/cc	0.939 g/cc	0.939 g/cc
Tensile Properties 1. Break strength 2. Break elongation	D6693 Type IV	40 kN/m 800%	53 kN/m 800%	66 kN/m 800%	80 kN/m 800%
Tear Resistance	D1004	150 N	200 N	250 N	300 N
Puncture Resistance	D4833	370 N	500 N	620 N	750 N
Carbon Black Content -%	D1603	2.0%	2.0%	2.0%	2.0%
Carbon Black Dispersion	D5596	Note (1)	Note (1)	Note (1)	Note (1)
Oxidative Induction Time (OIT)	D3895	100 min.	100 min.	100 min.	100 min.

(1). Canbon black dispersion (only near spherical agglomerates) for 10 different views:
9 in Categories 1 or 2 and 1 in Category 3