Properties	Test Method	GM SH075	GM SH100	GM SH125
Thickness	D5199	0.75 mm	1.00 mm	1.25 mm
Density	D1505	0.940 g/cc	0.940 g/cc	0.940 g/cc
Tensile Properties 1. Yield strength 2. Break strength 3. Yield elongation 4. Break elongation	D6693 Type IV	11 kN/m 20 kN/m 12% 700%	15 kN/m 27 kN/m 12% 700%	18 kN/m 33 kN/m 12% 700%
Tear Resistance	D1004	93 N	125 N	156 N
Puncture Resistance	D4833	240 N	320 N	400 N
Stress Crack Resistance	D5397 (App.)	300 hr.	300 hr.	300 hr.
Carbon Black Content	D1603	2.0%	2.0%	2.0%
Carbon Black Dispersion	D5596	Note (1)	Note (1)	Note (1)
Oxidative Induction Time (OIT)	D3895	100 min.	100 min.	100 min.

Properties	Test Method	GM SH150	GM SH200	GM SH250
Thickness	D5199	1.50 mm	2.00 mm	2.50 mm
Density	D1505	0.940 g/cc	0.940 g/cc	0.940 g/cc
Tensile Properties 1. Yield strength 2. Break strength 3. Yield elongation 4. Break elongation	D6693 Type IV	22 kN/m 40 kN/m 12% 700%	29 kN/m 53 kN/m 12% 700%	37 kN/m 67 kN/m 12% 700%
Tear Resistance	D1004	187 N	249 N	311 N
Puncture Resistance	D4833	480 N	640 N	800 N
Stress Crack Resistance	D5397 (App.)	300 hr.	300 hr.	300 hr.
Carbon Black Content	D1603	2.0%	2.0%	2.0%
Carbon Black Dispersion	D5596	Note (1)	Note (1)	Note (1)
Oxidative Induction Time (OIT)	D3895	100 min.	100 min.	100 min.

(1). Canbon black dispersion (only near spherical agglomerates) for 10
different views: 9 in Categories 1 or 2 and 1 in Category 3